电工钢硅钢片 M235-35 0.35*1000【修饰词

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

电工钢硅钢片：公称厚度(mm)的 100 倍。用于表示无取向电工钢的类型的字符，其中AV：普通型；AHV：型；AHV-M：高强度型；APV：高磁感型；AHS：高强度型 比总损耗 P1.0/400(W/kg)的 100 倍。小屈服强度（仅对应高强度型产品）宝钢英文名称 Baosteel 的首字母。Q/BQB 481－20213示例 1：B20AV1300 表示公称厚度为 0.20mm 的普通型无取向电工钢， 比总损耗 P1.0/400为 13W/kg；示例 2：B27AHV1400 表示公称厚度为 0.27mm 的型无取向电工钢， 比总损耗 P1.0/400为 14W/kg；示例 3：B30APV1500 表示公称厚度为 0.30mm 的高磁感型无取向电工钢， 比总损耗 P1.0/400为 15W/kg；示例 4：B25AHV1300M表示公称厚度为0.25mm的高强度型无取向电工钢， 比总损耗P1.0/400为13W/kg；示例 5：B35AHS500 表示公称厚度为 0.35mm 的高强度型无取向电工钢，小屈服强度 500MPa。5.3 绝缘涂层的分类和代号绝缘涂层的分类和代号应符合表2的规定。表 2 绝缘涂层的分类和代号绝缘涂层种类 代号 特征半有机薄涂层 A 改善冲片性，并有良好的焊接性半有机厚涂层 H 冲片性好，层间电阻高半有机无铬薄涂层 K 涂层中不含铬，具有良好的焊接性半有机无铬厚涂层 M 涂层中不含铬，具有良好的绝缘性能自粘接涂层 Z 涂层中不含铬，固化后具有良好的粘接性能，铁心固定强度大