取向硅钢片 0.3 B30G120承接

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

电工钢硅钢片叠装系数产品的叠装系数应符合表 3、安徽亳州附近表 4 的规定。供方如能保证，可不进行该试验。仲裁时，适用于无绝缘涂层状态。7.4.3 弯曲次数弯曲次数是指用肉眼在基板上观测到 次出现贯穿试样厚度的裂纹(或听到产生裂纹的声音)前的 反复弯曲次数，它表示材料的延展性。弯曲次数应符合表 3、安徽亳州附近表 4 的规定。供方如能保证，可不进行该试验。7.4.4 内应力产品应尽可能量避免出现内应力。内应力的检验不适用于宽度小于或等于150mm 的钢带（纵切分条后的钢带）。缝隙测量值应不超过 2mm。供方如能保证，可不进行该试验。8 检验和试验8.1 检验批次产品应按批验收，每个检验批应由不大于20吨的同牌号、安徽亳州附近同规格、安徽亳州附近同热处理状态、安徽亳州附近同绝缘涂层的钢带组成。对于重量大于20吨的钢带，每个钢卷组成一个检验批。

电工钢硅钢片硅钢是一种硅铁合金。用硅钢轧制的片材是电工领域中应用广的软磁材料，因而硅钢片又称电工钢片。硅钢片广泛用于电动机、发电机、变压器、扼流圈、电磁机构、继电器及测量仪表中电机工业大量使用厚度为0.35～0.50mm的硅钢片,用于：中型旋转机，压缩电机，通用马达，小型精密电机，电动汽车，压缩机，通用电机，电源变压器，精密变压器，节能电机，焊机变压器，稳压器，磁性密封器，加速器用电磁铁，汽车电机等；在电信高频技术中常用0.05~0.20mm的薄带钢片,以便更有效地降低涡流损耗。热轧硅钢片厚度为0.35～0.50mm，密度为7.55～7.70g/cm3,多用于大、中、小型交、直流电动机；冷轧无取向硅钢片厚度为0.35～0.50mm，密度为7.65～7.75g/cm3，多用于大型交流发电机、电动机，大、中、小型交、直流电动机；冷轧取向硅钢片厚度为0.23mm 0.27mm 0.3mm 0.35mm，密度为7.65g/cm3,多用于电力变压器、油浸式变压器，干式变压器，电抗器、磁放大器等；冷轧取向薄带厚度为0.05～0.20mm，多用于无线电高频变压器。